Chemical Composition
P650HS is a special non-mag, austenitic Mn-Cr-Mo-N-steel with a high pitting corrosion resistance, specifically developed for oilfield applications.
Mechanical Properties
To learn more about P650HS mechanical properties download the datasheet
Magnetic Properties
Relative permeability: < 1,005
Corrosion Resistance
Transgranular SCC: Prevented by special surface treatments (Hammer peening, roller burnishing, shot peening).
Intergranular SCC: The occurrence of material sensitization is prevented by quenching after warm-forging. Each collar is tested according to ASTM A 262, Pract. A and E, last edition.
Pitting Corrosion: Due to a high chromium-, molybdenum- and nitrogen contents a high resistance to pitting corrosion is given.
Non-Destructive testing
Magnetic inspection: Drill collars are 100% tested by a proprietary probe-testing process using a Forster Magnetomat 1.782. ("Hot Spot"-test).
Ultrasonic inspection: Each collar is ultrasonically inspected over 100% of the volume according to ASTM E 114, last edition as a minimum level.
P650HS Non-Mag Drill Collars meet all requirements of API Spec. 7.1, last edition. All tests are carried out according to ASTM-Standards, last editions.
Prepared / released: B. Holper- Date: June 2013